Accelerator (ACS-2200)
ACS - 2200 is generic curing accelerator used in all kinds of powder coatings to reduce curing or baking temperature or time with improved charging and mechanical properties of powder coating with out affecting finish and flow and smoothness of powder coating film. This accelerator is antiyellowing.
Typical Properties |
|
Appearance |
White Powder |
Use Level |
0.2 - 0.7 % of total premix formulation |
Volatile Content |
Less than 0.5 % |
Particle Size |
10 to 15 Micron |
Specific Gravity |
1.28 to 1.30 |
Starting formulations of Black Hybrid powder coating : |
||||
Gel Time ( Sec ) |
150 |
77 |
55 |
46 |
Epoxy Resin (EEW 750-850) |
30 |
30 |
30 |
30 |
Polyester Resin (AV 75-80) |
30 |
30 |
30 |
30 |
ACS-2200 |
0 |
0.3 |
0.5 |
0.7 |
Flow control agent (ACS-88) |
1 |
1 |
1 |
1 |
Benzoin |
0.4 |
0.4 |
0.4 |
0.4 |
Carbon Black (N220) |
1 |
1 |
1 |
1 |
Barium Sulphate Synthetic |
37.2 |
36.8 |
36.8 |
36.8 |
Total |
100 |
100 |
100 |
100 |
Applications |
• Coating produced with ACS -2200 are characterised by improved Mechanical properties, scratch resistance without affecting on gloss with good flow and surface smoothness. |
• Minimum cure schedule recommended is 10 min @160 Deg c (object temp ) depends on resin system. |
Packaging |
• Available in Polyethylene lined Bags net weight 25kg |
Shelf Life / Storage |
• Store at 25-30 deg C at RH - 60 % or cool and dry place to avoid moisture absorption. • Keep bag closed after use and keep away from fire. • Based on our experience the shelf life of this product is at Least one year when stored under dry and cool conditions. |
Note : The information herein is currently believed to be accurate. We do not guarantee its accuracy. Purchasers shall not rely on statements herein when purchasing any products.Purchasers should make their own investigations to determine if such products are suitable for a particular use. The products discussed are sold without warranty,express or implied, including a warranty of merchantability and fitness for use. Purchasers will be subjected to a separate agreement which will not incorporate this document.